Fast Setting, Strong Single Component Adhesive Excellent for Bonding, Caulking, Bedding and Sealing High UV Stability, Great Above and Below the Waterline.
High Bond Strength
45 Minutes Tack Free
12-24 Hours Full Cure
Permanent Elasticity
Non-Toxic and Odorless
Broad Temperature Stability (-40F to +212F)
Usage and Applications
Broad adhesion range (metal, glass fiber-
reinforced plastic, plastic,wood, glass)
Universal adhesive, sealant and joint filler
suitable for fiberglass, metals, wood and
building construction
Use for marine applications, car bodies,
thru hull fittings, corner jointing of aluminum
window frames, glazing with wood and
industrial assembly
In construction, use as an adhesive for
metal, glass fiber-reinforced plastic, plastics,
wood and glass
Great for interior finishing and sealing joints
High resistance to water, cleaning agents,
weak acids and alkalis
**Always pre-test hard to glue materials.
Not appropriate for bituminous surfaces,
polyolefins and Teflon.
Convenience
Uncomplicated, fast assembly thanks to strong, initial tack
Viscous and easy to apply in all positions
Fast hardening, get back to work faster
Sandable and over-coatable
Processing temperatures from 41F to 104F
Suitable for thermal processes(e.g. stove enameling, powder coating)
Application
Use a hand or pneumatic gun
Cut the nozzle to joint width
smooth over with a spatula, which when necessary can be moistened with a soap suds solution
Sandable and over-coatable
Clean up with Bio-Solv
Gentle for the Environment
Solvent Free and Plasticizer Free
Isocyanate-free and silicone free
Non-Toxic and Odorless
FLEX-BOND 5000 PRODUCT DATA :
APPLICATION DATA :
Base:
MS-Hybrid Polymer
Preparation:
Bonding surfaces must be dry, free from any dust, grease, oil, rust and any other dirt. Remove grease with an appropriate cleaning agent, e.g. BKP Solvent or Ebo clean.
Color:
White
Coatability:
With acrylic emulsion paints and baking varnish (subject to suitability tests)
Density:
1,41 g/cm³ at 20 °C
Application Temp.:
41 - 104 °F ( 5 - 40 °C component temperature)
Solids Content:
100%
Application method :
Use a hand or pneumatic caulking gun. Cut nozzle to suit joint width. Smooth over with a spatula which, when necessary, can be moistened in a soapsuds solution.
Stability:
Stable
Skin-forming time :
Approx. 10-15 minutes Curing time:
Dependent on depth of joint, temperature and level of moisture
Shore A hardness:
Approx. 57
Complete hardening:
1-2 mm per day, measured on a track under normal ambient conditions of 75 °F (23 °C / 65%)
Shrinkage:
Maximum 4%
Clean-up:
Use BKP Solvent for non-hardened adhesive, otherwise clean mechanically